挤出级HDPE 8380韩国韩华电线电缆**料

HANWHA CHNA-8380
高密度 (HMW) 聚乙烯
Hanwha Chemical
产品说明：

Hanwha CHNA-8380 is a high molecular weight, high density polyethylene(HDPE) insulation compound especially designed for high-speed wire insulating extrusion process. It provides excellent processability, environmental and thermal stress cracking resistance. It meets major international aging test specification for both solid and foam/skin insulation. It can be used for the full range of telephone cable insulation including air-core, jelly-filled and LAN cable (Cat. 5/5e).
HANWHA 8380 物性表
基本信息	
特性	
高 ESCR（抗应力开裂）高分子量高密度可加工性，良好
用途	
电线电缆应用通信电线绝缘材料
机构评级	
ASTM D 1248, III, Class A, Cat. 4, Grade E8ASTM D 1248, III, Class A, Cat. 4, Grade E9BS 6234 Type H03ICEA S-84-608IEC 60708NF C 32-060
形式	
粒子
加工方法	
电线&线缆挤出成型挤出
物理性能	额定值	单位制	测试方法
密度	0.945	g/cm3	ASTM D1505
熔流率（熔体流动速率） (190°C/2.16 kg)	0.70	g/10 min	ASTM D1238
抗环境应力开裂 (50°C, 10% Igepal, F0)	> 1000	hr	ASTM D1693
硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D, 1 秒)	53		ASTM D2240
机械性能	额定值	单位制	测试方法
抗张强度	23.5	MPa	ASTM D638
伸长率 (断裂)	550	%	ASTM D638
老化	额定值	单位制	测试方法
Oven Aging (100°C)	2.0	day	
拉伸强度保持率 - 2 days (100°C)	> 90	%	ASTM D638
伸长保持率 - 2 days (100°C)	> 90	%	ASTM D638
热性能	额定值	单位制	测试方法
耐热应力裂纹	> 96	hr	ASTM D2951
氧感应时间 - AI (200°C)	> 100	min	ASTM D3895
脆化温度	 1.0E+16	ohms·cm	ASTM D257
介电常数 (1 MHz)	< 2.30		ASTM D150
耗散因数 (1 MHz)	< 1.0E-4		ASTM D150
挤出	额定值	单位制	
熔体温度	240 到 280	°C